should i choose monel 400 or monel k-500? which scenes are they used in?
if you have the same confusion, you must read this article. it will let you understand all the same and different between monel 400 and monel k-500.
monel 400
monel® nickel-copper alloy 400 (uns n04400 / w.nr. 2.4360 and 2.4361) is a solid-solution alloy that can be hardened only by cold working. it has high strength and toughness over a wide temperature rangeand excellent resistance to many corrosive environments.
monel k-500
monel® alloy k-500 (uns n05500 / w.nr. 2.4375) is a nickel-copper alloy which combines the excellent corrosion resistance of monel alloy 400 with the added advantages of greater strength and hardness. the increased properties are obtained by adding aluminum and titanium to the nickel-copper base.
alloy 400 composition
trade name | astm/aisi alloy type | uns | %cu | %al | %ti | %fe | %mn | %si | %ni |
monel 400 | b 127, b 164 | n04400 | 28-34 | 2.5 max | 2.0 max | 0.5 max | 63 min |
monel alloy 400 melting point, density and tensile strength
density | melting point | tensile strength | yield strength (0.2%offset) | elongation | |
monel 400 | 8.8 g/cm3 | 1350 °c (2460 °f) | psi – 80000 , mpa – 550 | psi – 35000 , mpa – 240 | 40 % |
alloy 400 equivalent grades
standard | werkstoff nr. | uns | gost | afnor | jis | bs | en |
monel 400 | 2.4360 | n04400 | мнжмц 28-2,5-1,5 | nu-30m | nw 4400 | na 13 | nicu30fe |
monel k500 composition
trade name | astm/aisi alloy type | uns | %cu | %al | %ti | %fe | %mn | %si | %ni |
monel k-500 | b 865 | n05500 | 27-33 | 2.3-3.15 | 0.35-0.85 | 2.0 max | 1.5 max | 0.5 max | 63 min |
alloy k500 melting point, density and tensile strength
density | melting point | tensile strength | yield strength (0.2%offset) | elongation | |
monel k500 | 8.44 g/cm3 | 1350 °c (2460 °f) | psi – 160000 , mpa – 1100 | psi – 115000 , mpa – 790 | 20 % |
monel alloy k500 equivalent grades
standard | werkstoff nr. | uns | gost | afnor | jis | bs | en |
monel k500 | 2.4375 | n05500 |