| Standard | Outside Diameter | Wall Thickness | Weight |
| ASTM A 106 NF A 49-211 |
OD≤48.3; ±0,40mm 48.3<OD≤114.3; ±0.8mm 114.3<OD≤219.1; +1.6/-0.8mm OD>219.1; +2.4/-0.8mm |
+12.5% | +10/-3.5% for any length of pipe |
| EN 10216-2 hot rolled | ±1.0% or ±0.5mm (which is higher) | ±12.5% or ±0.4mm (which is higher) | |
| DIN 17175 hot rolled |
OD<=100 ± 0.75% (minimum±0.5mm) 100<OD<=320 ±0.9% |
OD <=130; WT≤ 2Sn; +15/-10% OD <=130; 2Sn<WT≤4Sn; +12.5/-10% OD <=130; WT>4Sn; ±9% 130<OD<=320; WT ≤0.05OD; +17.5/-12.5% 130<OD<=320; 0.05OD <WT≤0.11OD; ±12.5% 130<OD<=320; WT>0.11OD; ±10% Sn- Nominal wall thickness according to DIN 2448 |
+10/-8% for each tube ±7.5% for a lots over 10t |
| ASTM A210 hot rolled |
OD<=101.6+0.4/-0.8mm 101.6<OD<=190.5+0.4/-1.2mm 190.50<OD<=228.6+0.4/-1.6mm |
OD<=101.6 and WT<=2.4; +40%/0 OD<=101.6 and 2.4<WT<=3.8; +35%/0 OD<=101.6 and 3.8 <WT<=4.6; +33%/0 OD<=101.6 and WT>4.6; +28%/0 OD>101.6 and 2.4<WT<=3.8; +35%/0 OD>101.6 and 3.8 <WT<=4.6; +33%/0 OD>101.6 and WT>4.6; +28%/0 |
+16%/0 |
|
ASTM A213 hot rolled |
OD≤100mm: +0.4mm / -0.8 mm 100<OD ≤ 200mm: +0.4 /- 0.8 mm 200<OD ≤ 225mm: +0.4mm /-1.6 mm |
Average wall thickness: 10.3<WT≤73mm: +20%/-12.5% WT<73 mm & (WT/OD)≤5%: +22.5%/-12.5% WT<73 mm & (WT/OD)>5%: +15%/-12.5%
Minim wall thickness: WT ≤ 2.4 mm (only for OD ≤ 114.3 mm): + 40 % / -0% 2.4<WT≤3.8 mm: +35 %/-0% 3.8<WT≤4.6 mm: +33% / -0% WT>4.6 mm: +28% / -0%
|
– |
|
ASTM A213 Cold finished |
OD ≤25: +0.10 mm/-0.11 mm 25<OD ≤40mm: ±0.15 mm 40<OD <50mm: ±0.20 mm 50≤OD < 65mm: ±0.25 mm 65≤OD < 75 mm: ±0.30 mm 75≤OD ≤100 mm: ±0.38 mm 100<OD ≤200mm:+0.38/-0.64 mm 200<OD ≤225mm:+0.38 /-1.14 mm
|
Average wall thickness: ±10%
Minim wall thickness: For OD ≤38.1mm => WT = +20% / -0 For OD >38.1mm => WT= +22% / -0 |
|
|
ASTM A335 hot rolled |
For pipe ordered to NPS [DN] or outside diameter: 10.3<OD≤48.3mm: ±0.4 mm 48.3<OD ≤114.3mm: ± 0.8 mm 114.3<OD≤219.1 mm:+1.59 /-0.79mm 219.1<OD≤323.9mm:+2.38 mm /-0.79mm For pipe ordered to inside diameter: ±1% |
10.3<WT≤73mm: +20%/-12.5% WT<73 mm & (WT/OD)≤5%: +22.5%/-12.5% WT<73 mm & (WT/OD)>5%: +15%/-12.5%
|
|
| DIN 17175 cold rolled |
OD<=120± 0.6%(minimum±0.25mm) OD>120±0.75%
|
OD <=130; WT≤ 2Sn; +15/-10% OD <=130; 2Sn<WT≤4Sn; +12.5/-10% OD <=130; WT>4Sn; ±9% 130<OD<=320; WT ≤0.05OD; +17.5/-12.5% 130<OD<=320; 0.05OD <WT≤0.11OD; ±12.5% 130<OD<=320; WT>0.11OD; ±10% Sn – Nominal wall thickness according to DIN 2448 |
+10/-8% for each tube ±7.5% for a lots over 10t |
| EN 10216-2 cold rolled | ±0.5% or ±0.3mm (which is higher) | ±10% or ±0.2 mm (which is higher) | |
|
ASTM A179 and ASTM A210 cold rolled |
OD<25.4; ±0.10 25.4<=OD<=38.1; ±0.15 38.1<OD<50.8; ±0.20 50.8>=OD<63.5; ±0.25 63.5>=OD<76.2; ±0.30 |
OD<=38.1; +20% OD>38.1; +22% | OD<=38.1; +12% OD>38; +13% |